The FRP SYSTEM are wet lay up system using high-density carbon-fiber and pultruded laminate, E-AR glass or aramid strips glued to supports with special structural adhesives RESIN with superior mechanical characteristics. With both the plating and the wrapping methods of application, the system reinforces the structure where it is necessary to improve or restore static conditions, by increasing their resistance, load-bearing qualities and ductility, but without overloading the structure.
PRODUCTS
High standard and certified composite materials: carbon, Glass, Steel, Aramid to be used with adhesives RESIN
Carbon fabric uni-bi directional, quadriaxial C-SHEET, CTB, Q.
| Weight [g/m2] | 200-300-400-500-600 |
| Elastic modulus [GPa] | 240-390-640 |
| Tensile Strength [MPa] | 2600-3000-3800 |
| Elongation at break [%] | 0,5-0,8-1,8 |
Carbon pultruded laminates LAMELLA
| Thickness [mm] | 1,4 |
| Width [cm] | 5-10 |
| Elastic modulus [GPa] | > 160-200 |
| Tensile Strength [MPa] | > 2000-2500 |
| Elongation at break [%] | > 1,3-1,5 |
Carbon CFK pultruded rods unnotched and improved bond BARRA
| Diameter [mm] | 8-10-12 |
| Elastic modulus [GPa] | > 150 |
| Tensile Strength [MPa] | > 2300 |
| Elongation at break [%] | > 1,5 |
Basalt BFK 10R pultruded rods unnotched and improved bond BARRA
| Diameter [mm] | 10 |
| Elastic modulus [GPa] | > 50 |
| Tensile Strength [MPa] | > 800 |
| Elongation at break [%] | > 1,6 |
AFIX aramid fiber anchoring system connector
| Diameter [mm] | 6-8-10-12 |
| Elastic modulus [GPa] | 110 |
| Tensile Strength [MPa] | 1600 |
| Elongation at break [%] | 1,5 |
SFIX G galvanized steel anchor system connector
| Diameter [mm] | 5-10-12 |
| Elastic modulus [GPa] | 190 |
| Tensile Strength [MPa] | >2600 |
| Elongation at break [%] | >1,6 |
Aramid fabric uni-bi directional A-SHEET (filament)
| Weight [g/m²] | 300-400 |
| Elastic modulus [GPa] | 120 |
| Tensile Strength [MPa] | 2900 |
| Elongation at break [%] | 2,5 |
GALVANIZED STEEL FABRIC UHTSS uni-directional STEEL NET G
| TYPE | STEEL NET G 135 | STEEL NET G 220 | STEEL NET G 350 |
| Weight [g/m²] | 1350 | 2200 | 3500 |
| Elastic modulus [GPa] | 190 | 190 | 190 |
| Tensile Strength [MPa] | >2500 | >2500 | >2500 |
| Unit Tensile Strength [N/cm] | 4320 | 6980 | 11200 |
| Elongation at break [%] | >1,7 | >1,7 | >1,7 |
E-AR Glass fabric uni-bi directional G-SHEET
| Weight [g/m²] | 300-900 |
| GLASS TYPE (filament) | E | AR |
| Elastic modulus [GPa] | 73 | 70 |
| Tensile Strength [MPa] | >3000 | >2000 |
| Elongation at break [%] | 3-4 | >3 |
MAIN ADHESIVES
The following adhesives are technically approuved and certified to be used with carbon, glass, aramid and steel fabrics, laminates and rods.
The adhesives marked CE are produced according with EN 1504-4 european norm.
RESIN PRIMER primer bicomponent for porous surface.
RESIN PRIMER E primer bicomponent without solvent for any surface.
RESIN 90 special bicomponent adhesive to smooth surface and glue steel and laminate.
RESIN 75 special bicomponent adhesive to glue and impregnate fabric.
RESIN 70-75-98 and RESIN INJECT SF for rods anchoring and for injection into cracks.
EXTERNAL PROTECTION OF REINFORCED SYSTEM
Protection products for installed fabrics, laminate, steel:
RESINLAST bicomponent elastic paint.
RESINCOLOR anticarbonation paint.
Please check Company export dept for exact type of products available on production (weight, roll width, packaging): info@gpintech.com